Synthesis, characterization and up-conversion luminescence properties of α -NaYF4:Yb3+/Er3+/PVP/MOFs multilayer nanocrystals
العنوان: | Synthesis, characterization and up-conversion luminescence properties of α -NaYF4:Yb3+/Er3+/PVP/MOFs multilayer nanocrystals |
---|---|
المؤلفون: | Thi Kieu Giang Lam, Lukasz Marciniak, Quang Huy Tran, Manh Tien Dinh, Duc Chinh Vu, Vu Nguyen, Thu Huong Tran, Thi Khuyen Hoang, Thanh Huong Nguyen, Duc Roan Pham, Thanh Binh Nguyen, Quoc Minh Le |
المصدر: | Vietnam Journal of Science, Technology and Engineering, Vol 59, Iss 3 (2017) |
بيانات النشر: | Vietnam Ministry of Science and Technology, 2017. |
سنة النشر: | 2017 |
المجموعة: | LCC:Science |
مصطلحات موضوعية: | metal-organic frameworks, multilayer nanocrystals, self-template method, up-conversion, α -NaYF4:Yb3 /Er3 /PVP/MIL-100, α -NaYF4:Yb3 /Er3 / PVP/ZIF-8, Science |
الوصف: | The precursor PVP-capped α -NaYF4:Yb3+/Er3+ nanospheres were used as the templates for preparing the α -NaYF4:Yb3+/Er3+/PVP/MOFs multilayer nanocrystals with a self-template method. By using iron (III) carboxylate and zeolitic imidazolate frameworks dissolved in dimethylformamide (DMF) solution containing 25% of diethylene glycol (DEG), the sphericalshaped α -NaYF4:Yb3+/Er3+/PVP/MIL-100 and α -NaYF4:Yb3+/Er3+/PVP/ ZIF-8 multilayer nanocrystals were successfully prepared with the sizes of 300-500 nm at 100oC for one hour. Under a 976 nm laser excitation at room temperature, the α -NaYF4:Yb3+/Er3+/PVP/MIL-100 and α-NaYF4:Yb3+/ Er3+/PVP/ZIF-8 multilayer nanocrystals exhibited strong up-conversion luminescence with three emission bands centered at around 520 nm, 540 nm, and 655 nm corresponding to 2H11/2 → 4I15/2, 4S3/2 → 4I15/2, and 4F9/2 → 4I15/2 transitions of Er3+ ions, respectively. |
نوع الوثيقة: | article |
وصف الملف: | electronic resource |
اللغة: | English |
تدمد: | 2525-2461 2615-9937 |
Relation: | https://vietnamscience.vjst.vn/index.php/vjste/article/view/292; https://doaj.org/toc/2525-2461; https://doaj.org/toc/2615-9937 |
DOI: | 10.31276/VJSTE.59(3).79 |
URL الوصول: | https://doaj.org/article/05714c0e0347448f9ac5f5d5fd2da768 |
رقم الأكسشن: | edsdoj.05714c0e0347448f9ac5f5d5fd2da768 |
قاعدة البيانات: | Directory of Open Access Journals |
تدمد: | 25252461 26159937 |
---|---|
DOI: | 10.31276/VJSTE.59(3).79 |