The spheroidizing tendency and spheroidization mechanism of 75Cr1 steel
| العنوان: | The spheroidizing tendency and spheroidization mechanism of 75Cr1 steel |
|---|---|
| المؤلفون: | Huo Jiping, Zhou Chong, Wang Hua |
| المصدر: | MATEC Web of Conferences, Vol 242, p 01009 (2018) |
| بيانات النشر: | EDP Sciences, 2018. |
| سنة النشر: | 2018 |
| المجموعة: | LCC:Engineering (General). Civil engineering (General) |
| مصطلحات موضوعية: | Engineering (General). Civil engineering (General), TA1-2040 |
| الوصف: | Spheroidization annealing process was carried out on 75Cr1 steel after cold rolling. Using TEM, SEM and image analysis software Image-Pro Plus 6.0, the effects of cold rolling and spheroidization processes on microstructure and mechanical properties were analyzed. The result shows that the cold rolling leads to fragmentation of the cementite and formation of the defects, which induces faster lamellae break-up and accelerates the annealing process. With the increase of isothermal temperature and holding time, the dimension of the spheroidized carbides increase as driven by Ostwald ripening mechanism, whereas the hardness of the steel decreases. The prior cold rolling before annealing process causes the yield strength improve slightly, however shows little effect on the cold formability. The optimum heat treatment process is, holding the samples at 705oC for 6 hours with cold deformation ratio (ε) of 0.6. |
| نوع الوثيقة: | article |
| وصف الملف: | electronic resource |
| اللغة: | English French |
| تدمد: | 2261-236X |
| Relation: | https://doaj.org/toc/2261-236X |
| DOI: | 10.1051/matecconf/201824201009 |
| URL الوصول: | https://doaj.org/article/059118d196144144b81fdacef9fbbae2 |
| رقم الأكسشن: | edsdoj.059118d196144144b81fdacef9fbbae2 |
| قاعدة البيانات: | Directory of Open Access Journals |
Full Text Finder | تدمد: | 2261236X |
|---|---|
| DOI: | 10.1051/matecconf/201824201009 |