Preliminary In Vitro Study of Fluoride Release from Selected Ormocer Materials
العنوان: | Preliminary In Vitro Study of Fluoride Release from Selected Ormocer Materials |
---|---|
المؤلفون: | Piotr Kosior, Maciej Dobrzynski, Aneta Zakrzewska, Lukasz Grosman, Mariusz Korczynski, Tomasz Blicharski, Martina Gutbier, Adam Watras, Rafal J. Wiglusz |
المصدر: | Materials, Vol 14, Iss 9, p 2244 (2021) |
بيانات النشر: | MDPI AG, 2021. |
سنة النشر: | 2021 |
المجموعة: | LCC:Technology LCC:Electrical engineering. Electronics. Nuclear engineering LCC:Engineering (General). Civil engineering (General) LCC:Microscopy LCC:Descriptive and experimental mechanics |
مصطلحات موضوعية: | fluoride ion release, ormocer materials, fluoride recharge, Technology, Electrical engineering. Electronics. Nuclear engineering, TK1-9971, Engineering (General). Civil engineering (General), TA1-2040, Microscopy, QH201-278.5, Descriptive and experimental mechanics, QC120-168.85 |
الوصف: | The purpose of the in vitro study presented in this paper was to determine the long-term release of fluoride ions from selected ormocer materials (Admira (A), Admira Flow (AF), Admira Seal (AS)). The release of fluoride ions from these materials into a saline solution (0.9% NaCl) and deionized water was tested for 14 weeks. In a long-term study the measurements were taken after 1 and 3 h, then 1, 2, and 3 days and then at weekly intervals for 14 weeks. In a short-term study the measurements were made after 3, 24, 48, 72, 69, 168 h, i.e., within 7 days. All materials used in the test showed a constant level of fluoride release. The highest level of cumulative release of fluoride ions into deionized water was found in the AS material (23.95 ± 4.30 μg/mm2), slightly lower in the A material (23.26 ± 4.16 μg/mm2) and the lowest in the AF material (16.79 ± 2.26 μg/mm2). The highest level of cumulative release into saline solution was found in AF (8.08 ± 1.30 μg/mm2), slightly lower in AS (7.36 ± 0.30 μg/mm2) and the lowest in A (6.73 ± 1.10 μg /mm2). After 1 h of immersion of the samples in the saline solution, the highest level of fluoride was released by AF (0.57 ± 0.06 μg/mm2) followed by A (0.20 ± 0.03 μg/mm2) and AS (0.19 ± 0.02 µg/mm2). Moreover, in the 14-week study, the total amount of fluoride release into the saline, which imitates the environment of the oral cavity, was observed as the highest in the AF sample. |
نوع الوثيقة: | article |
وصف الملف: | electronic resource |
اللغة: | English |
تدمد: | 1996-1944 |
Relation: | https://www.mdpi.com/1996-1944/14/9/2244; https://doaj.org/toc/1996-1944 |
DOI: | 10.3390/ma14092244 |
URL الوصول: | https://doaj.org/article/146af327364a4a69a3866583c89b014f |
رقم الأكسشن: | edsdoj.146af327364a4a69a3866583c89b014f |
قاعدة البيانات: | Directory of Open Access Journals |
تدمد: | 19961944 |
---|---|
DOI: | 10.3390/ma14092244 |