Designing Symmetric Gradient Honeycomb Structures with Carbon-Coated Iron-Based Composites for High-Efficiency Microwave Absorption
العنوان: | Designing Symmetric Gradient Honeycomb Structures with Carbon-Coated Iron-Based Composites for High-Efficiency Microwave Absorption |
---|---|
المؤلفون: | Yu Zhang, Shu-Hao Yang, Yue Xin, Bo Cai, Peng-Fei Hu, Hai-Yang Dai, Chen-Ming Liang, Yun-Tong Meng, Ji-Hao Su, Xiao-Juan Zhang, Min Lu, Guang-Sheng Wang |
المصدر: | Nano-Micro Letters, Vol 16, Iss 1, Pp 1-18 (2024) |
بيانات النشر: | SpringerOpen, 2024. |
سنة النشر: | 2024 |
المجموعة: | LCC:Technology |
مصطلحات موضوعية: | MIL-88C (Fe), Fe/Fe3O4/Fe3C@C, Controllable preparation, Symmetric gradient honeycomb structure, Microwave absorbing, Technology |
الوصف: | Highlights MIL-88C (Fe) with varying aspect ratios as a precursor was synthesized by regulating oil bath conditions, followed by one-step thermal decomposition to obtain carbon-coated iron-based composites. High-efficiency microwave absorption properties were achieved with RL min value of -67.4 dB (2.13 mm) and wide effective absorption bandwidth (EAB) of 5.52 GHz (1.90 mm) under the low filler loading. A symmetric gradient honeycomb structure was constructed utilizing the high-frequency structure simulator, achieving an EAB of 14.6 GHz and a RL min of -59.0 dB. |
نوع الوثيقة: | article |
وصف الملف: | electronic resource |
اللغة: | English |
تدمد: | 2311-6706 2150-5551 |
Relation: | https://doaj.org/toc/2311-6706; https://doaj.org/toc/2150-5551 |
DOI: | 10.1007/s40820-024-01435-z |
URL الوصول: | https://doaj.org/article/18f4b7b093094b2992c7e1abb49615ee |
رقم الأكسشن: | edsdoj.18f4b7b093094b2992c7e1abb49615ee |
قاعدة البيانات: | Directory of Open Access Journals |
تدمد: | 23116706 21505551 |
---|---|
DOI: | 10.1007/s40820-024-01435-z |