MODIFICATION OF CALCIUM PHOSPHATE FOAM CERAMICS WITH BIOAPATITE IN SBF SOLUTION
| العنوان: | MODIFICATION OF CALCIUM PHOSPHATE FOAM CERAMICS WITH BIOAPATITE IN SBF SOLUTION |
|---|---|
| المؤلفون: | V.K. Krut’ko, L.Yu. Maslova, O.N. Musskaya, T.V. Safronova, A.I. Kulak |
| المصدر: | Физико-химические аспекты изучения кластеров, наноструктур и наноматериалов, Iss 13, Pp 870-880 (2021) |
| بيانات النشر: | Tver State University, 2021. |
| سنة النشر: | 2021 |
| المجموعة: | LCC:Physical and theoretical chemistry |
| مصطلحات موضوعية: | calcium phosphate foam ceramics, hydroxyapatite, polyurethane foam, tricalcium phosphate, sbf (simulated body fluid), bioapatite, Physical and theoretical chemistry, QD450-801 |
| الوصف: | The multiphase calcium phosphate foam ceramics, represented by β-tricalcium phosphate (65%) and β-calcium pyrophosphate (25%), including hydroxyapatite (5%) and α-tricalcium phosphate (5%), with 60-64% porosity and a through architecture of polyurethane foam was obtained. The application of a layer of hydroxyapatite led to an increase in the content of hydroxyapatite to 25%, α-tricalcium phosphate to 40%, and an increase in static strength to 0,03 MPa with a decrease in porosity to 49%. The application of the second layer of hydroxyapatite promoted an increase in the content of hydroxyapatite to 40%, the static strength reached 0,05 MPa at a porosity 40%. The bioapatite formation in the shape of «foam spheres» with a size from 2 to 10 μm occurred in the process of modifying all types of foam ceramics in a SBF solution during 21-28 days. The modified calcium phosphate foam ceramics enriched with α-tricalcium phosphate and hydroxyapatite, was characterized by the maximum static strength 0,08 MPa at a porosity 38%. |
| نوع الوثيقة: | article |
| وصف الملف: | electronic resource |
| اللغة: | Russian |
| تدمد: | 2226-4442 2658-4360 |
| Relation: | https://physchemaspects.ru/2021/doi-10-26456-pcascnn-2021-13-870/?lang=en; https://doaj.org/toc/2226-4442; https://doaj.org/toc/2658-4360 |
| DOI: | 10.26456/pcascnn/2021.13.870 |
| URL الوصول: | https://doaj.org/article/1aa45bede7184770889cc029766b490b |
| رقم الأكسشن: | edsdoj.1aa45bede7184770889cc029766b490b |
| قاعدة البيانات: | Directory of Open Access Journals |
Full Text Finder | تدمد: | 22264442 26584360 |
|---|---|
| DOI: | 10.26456/pcascnn/2021.13.870 |