In-situ Observation of High-Temperature Fracture Behaviour of 347 Stainless Steel Subjected to Simulated Welding Process
العنوان: | In-situ Observation of High-Temperature Fracture Behaviour of 347 Stainless Steel Subjected to Simulated Welding Process |
---|---|
المؤلفون: | Seok-Woo Ko, Hyeonwoo Park, Il Yoo, Hansoo Kim, Joonho Lee, Byoungchul Hwang |
المصدر: | Archives of Metallurgy and Materials, Vol vol. 66, Iss No 4, Pp 1019-1022 (2021) |
بيانات النشر: | Polish Academy of Sciences, 2021. |
سنة النشر: | 2021 |
المجموعة: | LCC:Mining engineering. Metallurgy LCC:Materials of engineering and construction. Mechanics of materials |
مصطلحات موضوعية: | 347 stainless steel, in-situ, high temperature, fracture behaviour, welding, confocal laser scanning microscope (clsm), Mining engineering. Metallurgy, TN1-997, Materials of engineering and construction. Mechanics of materials, TA401-492 |
الوصف: | In-situ study on the high-temperature fracture behaviour of 347 stainless steel was carried out by using a confocal laser scanning microscope (CLSM). The welding microstructures of the 347 stainless steel were simulated by subjecting the steel specimen to solution and aging treatments. Undissolved NbC carbides were present within grains after solution treatment, and M23C6 carbides were preferentially formed at grain boundaries after subsequent aging treatment. The M23C6 carbides formed at grain boundaries worked as stress concentration sites and thus generated larger cracks during high-temperature tensile testing. In addition, grain boundary embrittlement was found to be a dominant mechanism for the high-temperature fracture of the 347 stainless steel because vacancy diffusion in the Cr-depleted zones enhances intergranular fracture due to the precipitation of M23C6 carbides at grain boundaries. |
نوع الوثيقة: | article |
وصف الملف: | electronic resource |
اللغة: | English |
تدمد: | 2300-1909 |
Relation: | https://journals.pan.pl/Content/119290/PDF/AMM-2021-4-19-Byoungchul%20Hwang.pdf; https://doaj.org/toc/2300-1909 |
DOI: | 10.24425/amm.2021.136417 |
URL الوصول: | https://doaj.org/article/2885fa345aa84f00b346701f84139c49 |
رقم الأكسشن: | edsdoj.2885fa345aa84f00b346701f84139c49 |
قاعدة البيانات: | Directory of Open Access Journals |
تدمد: | 23001909 |
---|---|
DOI: | 10.24425/amm.2021.136417 |