Characterization of the Early Surface Films Dynamically Formed on Molten AZ91D and AM60B Alloys Under Different Atmospheres: A Comparative Study
العنوان: | Characterization of the Early Surface Films Dynamically Formed on Molten AZ91D and AM60B Alloys Under Different Atmospheres: A Comparative Study |
---|---|
المؤلفون: | Alireza Mirak |
المصدر: | Iranian Journal of Materials Science and Engineering, Vol 18, Iss 2, Pp 0-0 (2021) |
بيانات النشر: | Iran University of Science & Technology, 2021. |
سنة النشر: | 2021 |
المجموعة: | LCC:Technology |
مصطلحات موضوعية: | molten az91d and am60b alloys, fresh surface film, oxidation, fluoridation, Technology |
الوصف: | In the present study, the early stages of the surface oxidation and fluoridation of liquid AZ91D and AM60B alloys under ultra-high purity (UHP) argon, dry air, and air mixed with two different protective fluorine-bearing gases were studied. The chemical composition, morphology and thickness of the surface films formed inside the trapped bubbles were characterized by SEM and EDS analyses. It is found that the molten AM60B alloy is more sensitive to impurities under UHP argon gas than AZ91D alloy. Under dry air atmosphere, the entire surface of molten AZ91D alloy is covered with an oxide layer and thinner thickness than the surface film formed on AM60B alloy which has a rough surface exhibiting granular growth in later stages of oxidation. The EDS analyses show that film chemistry is mainly composed of Mg, Al, and O elements. Under fluorine-bearing gas/air mixtures with either SF6 or HFC-R134a at 3.5%vol., a fresh surface film formed with a flat and dense morphology of a uniform thickness composed of mixed Mg, F, Al, and O elements. It is observed that there is a lower O:F intensity ratio in the surface film formed on the molten AZ91D alloy under 1,1,1,2-tetra-fluoroethane (HFC-R134a) mixed with dry air compared to the AM60B alloy under both air/ R134a and air/SF6 mixtures which shows a higher fluorine concentration in the surface film a leading to a better oxidation resistance . |
نوع الوثيقة: | article |
وصف الملف: | electronic resource |
اللغة: | English |
تدمد: | 1735-0808 2383-3882 |
Relation: | http://ijmse.iust.ac.ir/article-1-1570-en.html; https://doaj.org/toc/1735-0808; https://doaj.org/toc/2383-3882 |
URL الوصول: | https://doaj.org/article/2f1e908041224415abe2d048318ee8a2 |
رقم الأكسشن: | edsdoj.2f1e908041224415abe2d048318ee8a2 |
قاعدة البيانات: | Directory of Open Access Journals |
تدمد: | 17350808 23833882 |
---|