دورية أكاديمية
Fracture Resistance of a Two-Piece Zirconia Implant System after Artificial Loading and/or Hydrothermal Aging—An In Vitro Investigation
العنوان: | Fracture Resistance of a Two-Piece Zirconia Implant System after Artificial Loading and/or Hydrothermal Aging—An In Vitro Investigation |
---|---|
المؤلفون: | Ralf-Joachim Kohal, Tim Schikofski, Erik Adolfsson, Kirstin Vach, Sebastian Berthold Maximilian Patzelt, Julian Nold, Gregor Wemken |
المصدر: | Journal of Functional Biomaterials, Vol 14, Iss 12, p 567 (2023) |
بيانات النشر: | MDPI AG, 2023. |
سنة النشر: | 2023 |
المجموعة: | LCC:Biotechnology LCC:Medicine (General) |
مصطلحات موضوعية: | zirconia oral implants, loading, aging, Biotechnology, TP248.13-248.65, Medicine (General), R5-920 |
الوصف: | The purpose of the present study was to assess the fracture resistance of a two-piece alumina-toughened zirconia implant system with a carbon-reinforced PEEK abutment screw. Methods: Thirty-two implants with screw-retained zirconia abutments were divided into four groups of eight samples each. Group 0 (control group) was neither loaded nor aged in a chewing simulator; group H was hydrothermally aged; group L was loaded with 98 N; and group HL was subjected to both hydrothermal aging and loading in a chewing simulator. One sample of each group was evaluated for t-m phase transformation, and the others were loaded until fracture. A one-way ANOVA was applied to evaluate differences between the groups. Results: No implant fracture occurred during the artificial chewing simulation. Furthermore, there were no statistically significant differences (p > 0.05) between the groups in terms of fracture resistance (group 0: 783 ± 43 N; group H: 742 ± 43 N; group L: 757 ± 86 N; group HL: 740 ± 43 N) and bending moment (group 0: 433 ± 26 Ncm; group H: 413 ± 23 Ncm; group L: 422 ± 49 Ncm; group HL: 408 ± 27 Ncm). Conclusions: Within the limitations of the present investigation, it can be concluded that artificial loading and hydrothermal aging do not reduce the fracture resistance of the investigated implant system. |
نوع الوثيقة: | article |
وصف الملف: | electronic resource |
اللغة: | English |
تدمد: | 2079-4983 |
Relation: | https://www.mdpi.com/2079-4983/14/12/567; https://doaj.org/toc/2079-4983 |
DOI: | 10.3390/jfb14120567 |
URL الوصول: | https://doaj.org/article/321e0a273b5c4d299c5e3cbee4562139 |
رقم الأكسشن: | edsdoj.321e0a273b5c4d299c5e3cbee4562139 |
قاعدة البيانات: | Directory of Open Access Journals |
تدمد: | 20794983 |
---|---|
DOI: | 10.3390/jfb14120567 |