Tunable polarization-drived high energy storage performances in flexible PbZrO3 films by growing Al2O3 nanolayers
العنوان: | Tunable polarization-drived high energy storage performances in flexible PbZrO3 films by growing Al2O3 nanolayers |
---|---|
المؤلفون: | Chao Yin, Tiandong Zhang, Zhuangzhuang Shi, Bowen Zhang, Changhai Zhang, Qingguo Chi |
المصدر: | Journal of Advanced Ceramics, Vol 12, Iss 11, Pp 2123-2133 (2023) |
بيانات النشر: | Tsinghua University Press, 2023. |
سنة النشر: | 2023 |
المجموعة: | LCC:Clay industries. Ceramics. Glass |
مصطلحات موضوعية: | sol–gel, flexible, antiferroelectric, polarization, energy storage, Clay industries. Ceramics. Glass, TP785-869 |
الوصف: | In recent years, PbZrO3 (PZO) films have become favorable electric storage materials due to the unique electric field-induced phase transition behavior, but the severe hysteresis effect leads to low energy storage density and efficiency. In this work, inserting Al2O3 (AO) insulation nanolayers is proposed to tune the polarization behavior of flexible PZO films, anticipating optimization of energy storage performance. The results show that the thickness of the AO nanolayers has a deep influence on the polarization behavior of the PZO films, and PZO/AO/PZO (PAP) sandwiched films with 8 nm AO interlayer deliver relaxor ferroelectric-like polarization instead of antiferroelectric counterpart. To further utilize the AO nanolayers as top/bottom layers, the linear-like polarization and the highest breakdown strength are achieved in the AO/PZO/AO/PZO/AO (APAPA8) multilayer films, leading to both high discharged energy storage density of 35.2 J/cm3 and efficiency of 92.9%, as well as excellent fatigue and bending endurance, good temperatures, and frequency stability. The tunable polarization induced by growing the AO nanolayers makes antiferroelectric PZO films have great potential to be used as energy storage dielectrics. |
نوع الوثيقة: | article |
وصف الملف: | electronic resource |
اللغة: | English |
تدمد: | 2226-4108 2227-8508 |
Relation: | https://www.sciopen.com/article/10.26599/JAC.2023.9220814; https://doaj.org/toc/2226-4108; https://doaj.org/toc/2227-8508 |
DOI: | 10.26599/JAC.2023.9220814 |
URL الوصول: | https://doaj.org/article/e3601dd5430741c2998dc284cafd1d10 |
رقم الأكسشن: | edsdoj.3601dd5430741c2998dc284cafd1d10 |
قاعدة البيانات: | Directory of Open Access Journals |
تدمد: | 22264108 22278508 |
---|---|
DOI: | 10.26599/JAC.2023.9220814 |