دورية أكاديمية
Analysis of Mechanical Properties of Welded Joint Metal from TPP Steam Piping after Its Operational Degradation and Hydrogenation
العنوان: | Analysis of Mechanical Properties of Welded Joint Metal from TPP Steam Piping after Its Operational Degradation and Hydrogenation |
---|---|
المؤلفون: | Volodymyr Hutsaylyuk, Oleksandra Student, Pavlo Maruschak, Halyna Krechkovska, Olha Zvirko, Lesya Svirska, Ivan Tsybailo |
المصدر: | Materials, Vol 16, Iss 24, p 7520 (2023) |
بيانات النشر: | MDPI AG, 2023. |
سنة النشر: | 2023 |
المجموعة: | LCC:Technology LCC:Electrical engineering. Electronics. Nuclear engineering LCC:Engineering (General). Civil engineering (General) LCC:Microscopy LCC:Descriptive and experimental mechanics |
مصطلحات موضوعية: | heat-resistant steel, welded joint, thermal power plant, hydrogenation, operational degradation, mechanical properties, Technology, Electrical engineering. Electronics. Nuclear engineering, TK1-9971, Engineering (General). Civil engineering (General), TA1-2040, Microscopy, QH201-278.5, Descriptive and experimental mechanics, QC120-168.85 |
الوصف: | In this paper, the mechanical properties of various zones of the welded joints of a heat-resistant steel 15Kh1M1F in different states (in the initial state, after an operation on the main steam piping of a thermal power plant (TPP) for 23 years) were determined, and the fracture surfaces were analyzed using scanning electron microscopy (SEM) images. The effect of hydrogen electrolytic charging on mechanical behavior and fracture mechanism was also studied. The long-term operation of welds resulted in a higher degradation degree of the weld metal compared to the base one, indicated by the deterioration of mechanical properties: decrease in hardness, strength characteristics, and reduction in area, which was accompanied by an atypical increase in elongation at fracture. All studied zones of the operated welded joints were characterized by higher hydrogen content, 2.5–3 times higher than that in the initial state. Additional hydrogen charging of the weld joint metal led to a decrease in the strength and ductility characteristics, more significantly for the operated weld compared with the non-operated one. This justified the possibility of using short-term tests of hydrogenated WM in the air to assess the degree of its damage during operation on a steam piping. |
نوع الوثيقة: | article |
وصف الملف: | electronic resource |
اللغة: | English |
تدمد: | 1996-1944 |
Relation: | https://www.mdpi.com/1996-1944/16/24/7520; https://doaj.org/toc/1996-1944 |
DOI: | 10.3390/ma16247520 |
URL الوصول: | https://doaj.org/article/d388cd95ee4448f2bcfed1051b72746a |
رقم الأكسشن: | edsdoj.388cd95ee4448f2bcfed1051b72746a |
قاعدة البيانات: | Directory of Open Access Journals |
تدمد: | 19961944 |
---|---|
DOI: | 10.3390/ma16247520 |