Laser Welding of Titanium/Steel Bimetallic Sheets with In Situ Formation of Fex(CoCrNiMn)Tiy High-Entropy Alloys in Weld Metal
| العنوان: | Laser Welding of Titanium/Steel Bimetallic Sheets with In Situ Formation of Fex(CoCrNiMn)Tiy High-Entropy Alloys in Weld Metal |
|---|---|
| المؤلفون: | Dejia Liu, Zhe Ma, Nianlong Xue, Weixiong Wang, Shanguo Han |
| المصدر: | Materials, Vol 17, Iss 3, p 623 (2024) |
| بيانات النشر: | MDPI AG, 2024. |
| سنة النشر: | 2024 |
| المجموعة: | LCC:Technology LCC:Electrical engineering. Electronics. Nuclear engineering LCC:Engineering (General). Civil engineering (General) LCC:Microscopy LCC:Descriptive and experimental mechanics |
| مصطلحات موضوعية: | TA1/Q345 bimetallic sheets, high-entropy alloys, microstructure, mechanical properties, Technology, Electrical engineering. Electronics. Nuclear engineering, TK1-9971, Engineering (General). Civil engineering (General), TA1-2040, Microscopy, QH201-278.5, Descriptive and experimental mechanics, QC120-168.85 |
| الوصف: | Due to the notable disparities in the physical and chemical characteristics between titanium and steel, the direct fusion of titanium/steel bimetallic sheets results in a considerable formation of fragile intermetallic compounds, making it difficult to achieve excellent metallurgical welded joints. In this study, a multi-principal powder of CoCrNiMn was designed and utilized as a filler material in the welding of the TA1/Q345 bimetallic sheet. It was expected that the in situ formation of Fex(CoCrNiMn)Tiy high-entropy alloys would be achieved using the filler powders, combined with the Ti and Fe elements from the melting of the TA1 and Q345 so as to restrain the generation of Fe-Ti IMCs and obtain the promising welded joints of the TA1/Q345 bimetallic sheet. An interesting finding is that high-entropy alloys were successfully obtained in the weld metal. The Fe-Ti intermetallic compounds at the welding interface were significantly reduced. The tensile strength was ~293 MPa, accounting for 60% of the strength of the base metal. Dimples were observed at the fracture of the welded joint. |
| نوع الوثيقة: | article |
| وصف الملف: | electronic resource |
| اللغة: | English |
| تدمد: | 1996-1944 |
| Relation: | https://www.mdpi.com/1996-1944/17/3/623; https://doaj.org/toc/1996-1944 |
| DOI: | 10.3390/ma17030623 |
| URL الوصول: | https://doaj.org/article/c40467086ab544f985f220da5d21c10a |
| رقم الأكسشن: | edsdoj.40467086ab544f985f220da5d21c10a |
| قاعدة البيانات: | Directory of Open Access Journals |
Full Text Finder | تدمد: | 19961944 |
|---|---|
| DOI: | 10.3390/ma17030623 |