Effects of Actual Marine Atmospheric Pre-Corrosion and Pre-Fatigue on the Fatigue Property of 7085 Aluminum Alloy
العنوان: | Effects of Actual Marine Atmospheric Pre-Corrosion and Pre-Fatigue on the Fatigue Property of 7085 Aluminum Alloy |
---|---|
المؤلفون: | Laixin Shi, Lin Xiang, Jianquan Tao, Jun Liu, Qiang Chen, Yong Zhong |
المصدر: | Metals, Vol 12, Iss 1, p 81 (2022) |
بيانات النشر: | MDPI AG, 2022. |
سنة النشر: | 2022 |
المجموعة: | LCC:Mining engineering. Metallurgy |
مصطلحات موضوعية: | 7085 aluminum alloy, actual marine atmospheric environment, outdoor exposure test, corrosion, fatigue, Mining engineering. Metallurgy, TN1-997 |
الوصف: | Effects of actual marine atmospheric precorrosion and prefatigue on the fatigue property of 7085-T7452 aluminum alloy were investigated by using the methods of marine atmospheric outdoor exposure tests and constant amplitude axial fatigue tests. Marine atmospheric corrosion morphologies, fatigue life, and fatigue fractography were analyzed. After three months of outdoor exposure, both pitting corrosion and intergranular corrosion (IGC) occurred, while the latter was the dominant marine atmospheric corrosion mode. Marine atmospheric precorrosion could result in a dramatical decrease in the fatigue life of the as-received 7085-T7452 aluminum alloy, while selective prefatigue can improve the total fatigue life of the precorroded specimen. The mechanism of the actual marine atmospheric corrosion and its effects on the fatigue life of the 7085-T7452 aluminum alloy were also discussed. |
نوع الوثيقة: | article |
وصف الملف: | electronic resource |
اللغة: | English |
تدمد: | 12010081 2075-4701 |
Relation: | https://www.mdpi.com/2075-4701/12/1/81; https://doaj.org/toc/2075-4701 |
DOI: | 10.3390/met12010081 |
URL الوصول: | https://doaj.org/article/46aa131ed4af4038974184cae93bcac0 |
رقم الأكسشن: | edsdoj.46aa131ed4af4038974184cae93bcac0 |
قاعدة البيانات: | Directory of Open Access Journals |
تدمد: | 12010081 20754701 |
---|---|
DOI: | 10.3390/met12010081 |