Hot Deformation Behavior of Haynes 25 by the Hot Tensile Test
العنوان: | Hot Deformation Behavior of Haynes 25 by the Hot Tensile Test |
---|---|
المؤلفون: | M. Samii Zafarghandi, S. M. Abbasi |
المصدر: | Journal of Advanced Materials in Engineering, Vol 38, Iss 2, Pp 1-10 (2019) |
بيانات النشر: | Isfahan University of Technology, 2019. |
سنة النشر: | 2019 |
المجموعة: | LCC:Materials of engineering and construction. Mechanics of materials |
مصطلحات موضوعية: | superalloy, hot deformation, carbide, ductility, dynamic recrystallization., Materials of engineering and construction. Mechanics of materials, TA401-492 |
الوصف: | In the present work, hot tensile behavior of Haynes 25 Co-base alloy was investigated in the temperature range of 950-1200 ˚C and 0.1 s-1. Thermodynamic calculations showed that M23C6 and M6C carbides were stable below 1000 ˚C and above 1050 ˚C, respectively. Stress-strain curves also indicated an unusual trend of strain fracture. It was observed that with increasing temperature from 950 to 1050 ˚C, the fracture strain was decreased, while it was raised above 1050 ˚C again. Increasing the volume fraction of M6C carbide rich in Tungsten resulted in the loss of ductility. Also, microstructural evaluations showed dynamic recrystallization (DRX) grains were nucleated and growth was around carbides and the initial grains at 1150 ˚C. Occurrence of DRX led to the improvement of ductility via grain refinement mechanism, so this alloy had the highest level of ductility at 1150 ˚C |
نوع الوثيقة: | article |
وصف الملف: | electronic resource |
اللغة: | Persian |
تدمد: | 2251-600X 2423-5733 |
Relation: | http://jame.iut.ac.ir/article-1-987-en.html; https://doaj.org/toc/2251-600X; https://doaj.org/toc/2423-5733 |
URL الوصول: | https://doaj.org/article/4773a7e742544d47b0782f72d82add79 |
رقم الأكسشن: | edsdoj.4773a7e742544d47b0782f72d82add79 |
قاعدة البيانات: | Directory of Open Access Journals |
تدمد: | 2251600X 24235733 |
---|