Analysis of the Long-Term Corrosion Behavior of X80 Pipeline Steel in Acidic Red Soil Using Electrical Resistance Test Technique
العنوان: | Analysis of the Long-Term Corrosion Behavior of X80 Pipeline Steel in Acidic Red Soil Using Electrical Resistance Test Technique |
---|---|
المؤلفون: | Shuaixing Wang, Daoxin Liu, Nan Du, Qing Zhao, Jinhua Xiao |
المصدر: | Advances in Materials Science and Engineering, Vol 2015 (2015) |
بيانات النشر: | Wiley, 2015. |
سنة النشر: | 2015 |
المجموعة: | LCC:Materials of engineering and construction. Mechanics of materials |
مصطلحات موضوعية: | Materials of engineering and construction. Mechanics of materials, TA401-492 |
الوصف: | The long-term corrosion rate of X80 steel in an acidic red soil was monitored in situ by using a precise electrical resistance (ER) test system. The corrosion characteristics of X80 steel were examined via SEM, EDS, and XRD. The results indicated that the corrosion rate determined from ER test was very similar to that obtained from the mass loss test. The ER test technique made it possible to predict the long-term corrosion rate of steel in soil in situ. The corrosion rate of X80 steel in acidic red soil was about 0.0902 mm/a at 38 weeks, but the corrosion rate was dropped to 0.0226 mm/a after 5 years. The final corrosion product layer was composed mainly of FeOOH, γ-Fe2O3, and FeCO3. |
نوع الوثيقة: | article |
وصف الملف: | electronic resource |
اللغة: | English |
تدمد: | 1687-8434 1687-8442 |
Relation: | https://doaj.org/toc/1687-8434; https://doaj.org/toc/1687-8442 |
DOI: | 10.1155/2015/931761 |
URL الوصول: | https://doaj.org/article/4b0e74f0612d48f6b5be75210eb94866 |
رقم الأكسشن: | edsdoj.4b0e74f0612d48f6b5be75210eb94866 |
قاعدة البيانات: | Directory of Open Access Journals |
تدمد: | 16878434 16878442 |
---|---|
DOI: | 10.1155/2015/931761 |