Influence of Hot Plastic Deformation in γ and (γ + α) Area on the Structure and Mechanical Properties of High-Strength Low-Alloy (HSLA) Steel
العنوان: | Influence of Hot Plastic Deformation in γ and (γ + α) Area on the Structure and Mechanical Properties of High-Strength Low-Alloy (HSLA) Steel |
---|---|
المؤلفون: | Jan Sas, Tibor Kvačkaj, Ondrej Milkovič, Michal Zemko |
المصدر: | Materials, Vol 9, Iss 12, p 971 (2016) |
بيانات النشر: | MDPI AG, 2016. |
سنة النشر: | 2016 |
المجموعة: | LCC:Technology LCC:Electrical engineering. Electronics. Nuclear engineering LCC:Engineering (General). Civil engineering (General) LCC:Microscopy LCC:Descriptive and experimental mechanics |
مصطلحات موضوعية: | high-strength low-alloy (HSLA) steel, controlled rolling, mechanical properties, microstructure, dual-phase region, Technology, Electrical engineering. Electronics. Nuclear engineering, TK1-9971, Engineering (General). Civil engineering (General), TA1-2040, Microscopy, QH201-278.5, Descriptive and experimental mechanics, QC120-168.85 |
الوصف: | The main goal of this study was to develop a new processing technology for a high-strength low-alloy (HSLA) steel in order to maximize the mechanical properties attainable at its low alloy levels. Samples of the steel were processed using thermal deformation schedules carried out in single-phase (γ) and dual-phase (γ + α) regions. The samples were rolled at unconventional finishing temperatures, their final mechanical properties were measured, and their strength and plasticity behavior was analyzed. The resulting microstructures were observed using optical and transmission electron microscopy (TEM). They consisted of martensite, ferrite and (NbV)CN precipitates. The study also explored the process of ferrite formation and its influence on the mechanical properties of the material. |
نوع الوثيقة: | article |
وصف الملف: | electronic resource |
اللغة: | English |
تدمد: | 1996-1944 |
Relation: | http://www.mdpi.com/1996-1944/9/12/971; https://doaj.org/toc/1996-1944 |
DOI: | 10.3390/ma9120971 |
URL الوصول: | https://doaj.org/article/ade51576393d4cb688131977dd7d2d98 |
رقم الأكسشن: | edsdoj.51576393d4cb688131977dd7d2d98 |
قاعدة البيانات: | Directory of Open Access Journals |
تدمد: | 19961944 |
---|---|
DOI: | 10.3390/ma9120971 |