Ultraviolet resistance on weft knitted fabric coated by benzotriazoles
العنوان: | Ultraviolet resistance on weft knitted fabric coated by benzotriazoles |
---|---|
المؤلفون: | Tuan Anh Nguyen, Nhu Tram Nguyen Nu |
المصدر: | Fashion and Textiles, Vol 11, Iss 1, Pp 1-13 (2024) |
بيانات النشر: | SpringerOpen, 2024. |
سنة النشر: | 2024 |
المجموعة: | LCC:Textile bleaching, dyeing, printing, etc. LCC:Social Sciences |
مصطلحات موضوعية: | Ultraviolet protection, Weft knitted fabric, Benzotriazoles (BTZ), Cotton fabric, Ultraviolet protection factor (UPF), Textile bleaching, dyeing, printing, etc., TP890-933, Social Sciences |
الوصف: | Abstract Ultraviolet resistance upon four different types of weft knitted fabrics including Lacoste, Single Jersey, Rib and Interlock were experimentally measured and evaluated by ultraviolet–visible spectroscopy under effects of gauge, specific weight, fiber composition and finishing agent as benzotriazole derivatives. The results showed that ultraviolet protection factor (UPF) of Interlock sample reached the highest value at 42.7. Simultaneously, the higher gauge of Single Jersey knitted fabrics was, the better its ultraviolet protection exhibited. Also, insertion of polyester fibers or spandex fibers into cotton knitted fabrics with a certain ratio strongly increased UPF values. Notably, all UPFs of coated fabrics with a given content of benzotriazole were significantly improved and almost coated samples could undergo several washing cycles and still retain their inherent breathability. This work demonstrated that cotton knitted fabrics coated with benzotriazoles were excellently enhanced ultraviolet protection. Especially, the UPF values on Interlock or Rib specimens as well as Single Jersey samples blended with polyester/spandex fibers were found to be higher than 15. |
نوع الوثيقة: | article |
وصف الملف: | electronic resource |
اللغة: | English |
تدمد: | 2198-0802 |
Relation: | https://doaj.org/toc/2198-0802 |
DOI: | 10.1186/s40691-024-00376-w |
URL الوصول: | https://doaj.org/article/53202896281a4261ad19397dc9a10348 |
رقم الأكسشن: | edsdoj.53202896281a4261ad19397dc9a10348 |
قاعدة البيانات: | Directory of Open Access Journals |
تدمد: | 21980802 |
---|---|
DOI: | 10.1186/s40691-024-00376-w |