Optimization of high Nb-TiAl alloy impeller investment casting based on ProCAST software
العنوان: | Optimization of high Nb-TiAl alloy impeller investment casting based on ProCAST software |
---|---|
المؤلفون: | LIU Jinhu, JI Zhijun, LI Feng, FENG Xin, YU Wen, DING Xianfei, NAN Hai |
المصدر: | Journal of Aeronautical Materials, Vol 41, Iss 2, Pp 61-71 (2021) |
بيانات النشر: | Journal of Aeronautical Materials, 2021. |
سنة النشر: | 2021 |
المجموعة: | LCC:Motor vehicles. Aeronautics. Astronautics |
مصطلحات موضوعية: | procast, high nb-tial alloy, impeller, numerical simulation, investment casting, Motor vehicles. Aeronautics. Astronautics, TL1-4050 |
الوصف: | The casting simulation software ProCAST was used to achieve the simulation of the filling and solidification process of the high Nb-TiAl alloy impeller investment casting. The influence of the casting and filling process on the filling and solidification characteristics of alloy melt filling, shrinkage cavity and porosity was studied, and the corresponding process was optimized. The casting test and the non-destructive testing analysis of the casting were carried out, and the anatomical analysis of the casting was performed to verify the distribution of the shrinkage cavity and porosity. The mechanical properties of the impeller at room temperature and high temperature were studied using attached test rods. The results show that ProCAST software is more accurate in predicting shrinkage cavity and porosity of the high Nb-TiAl casting, and the process scheme is optimized by simulation and prediction results to avoid the formation of large shrinkage cavity and porosity in casting, only micro shrinkage cavity less than 22 μm is existed in the final casting. All castings are fully filled, with the tensile strength about 580 MPa at room temperature and about 450 MPa at high temperature of 850 ℃. |
نوع الوثيقة: | article |
وصف الملف: | electronic resource |
اللغة: | Chinese |
تدمد: | 1005-5053 49756710 |
Relation: | https://doaj.org/toc/1005-5053 |
DOI: | 10.11868/j.issn.1005-5053.2020.000058 |
URL الوصول: | https://doaj.org/article/571bf337a0544b299a38c497567103f3 |
رقم الأكسشن: | edsdoj.571bf337a0544b299a38c497567103f3 |
قاعدة البيانات: | Directory of Open Access Journals |
تدمد: | 10055053 49756710 |
---|---|
DOI: | 10.11868/j.issn.1005-5053.2020.000058 |