Synthesis of High-performance LiNi0.6Co0.2Mn0.2O2 Cathode Material for Lithium-ion Batteries by Using a Four Times Liquid Nitrogen Quenching Method and an Al2O3 Coating Method
العنوان: | Synthesis of High-performance LiNi0.6Co0.2Mn0.2O2 Cathode Material for Lithium-ion Batteries by Using a Four Times Liquid Nitrogen Quenching Method and an Al2O3 Coating Method |
---|---|
المؤلفون: | Wenyuan Yang, Yinze Zuo, Qi Chen, Yan Zhang |
المصدر: | Materials, Vol 12, Iss 22, p 3666 (2019) |
بيانات النشر: | MDPI AG, 2019. |
سنة النشر: | 2019 |
المجموعة: | LCC:Technology LCC:Electrical engineering. Electronics. Nuclear engineering LCC:Engineering (General). Civil engineering (General) LCC:Microscopy LCC:Descriptive and experimental mechanics |
مصطلحات موضوعية: | lithium ion batteries, lini0.6co0.2mn0.2o2, liquid nitrogen, al2o3, electrochemical performance, Technology, Electrical engineering. Electronics. Nuclear engineering, TK1-9971, Engineering (General). Civil engineering (General), TA1-2040, Microscopy, QH201-278.5, Descriptive and experimental mechanics, QC120-168.85 |
الوصف: | Based on the normal co-precipitation method to synthesize LiNi0.6Co0.2Mn0.2O2 cathode material, we propose a novel approach using a liquid nitrogen quenching method to synthesize Al2O3 coated LiNi0.6Co0.2Mn0.2O2 cathode material. In the whole process, liquid nitrogen was used four times to quench the materials from high temperatures (50 °C, 750 °C, 90 °C, 500 °C) to −196 °C rapidly in four stages. Various characterizations proved that this method could help to improve the electrochemical performance of lithium-ion batteries. Especially at 5 C rate current, after 100 cycles, the specific discharge capacities were 24.5 mAh/g (LNCM 622), 43.8 mAh/g (LNCM 622-LN), and 53.9 mAh/g (LNCM 622-LN@Al2O3). Liquid N2 quenching increased the charge/discharge capacities and the Al2O3 layer increased the cycle stability at high current, to finally obtain improved electrochemical properties. |
نوع الوثيقة: | article |
وصف الملف: | electronic resource |
اللغة: | English |
تدمد: | 1996-1944 |
Relation: | https://www.mdpi.com/1996-1944/12/22/3666; https://doaj.org/toc/1996-1944 |
DOI: | 10.3390/ma12223666 |
URL الوصول: | https://doaj.org/article/a5c992a1e1c34b7a8e459e2070404b9b |
رقم الأكسشن: | edsdoj.5c992a1e1c34b7a8e459e2070404b9b |
قاعدة البيانات: | Directory of Open Access Journals |
تدمد: | 19961944 |
---|---|
DOI: | 10.3390/ma12223666 |