Comparative evaluation of physical and chemical properties of calcium silicate-based root-end filling materials (Mineral trioxide aggregate and biodentine): An in vitro study
| العنوان: | Comparative evaluation of physical and chemical properties of calcium silicate-based root-end filling materials (Mineral trioxide aggregate and biodentine): An in vitro study |
|---|---|
| المؤلفون: | Shilpa Kumari, Anika Mittal, Shifali Dadu, Aditi Dhaundiyal, Anju Abraham, Bidya Yendrembam |
| المصدر: | Indian Journal of Dental Sciences, Vol 10, Iss 4, Pp 197-202 (2018) |
| بيانات النشر: | Wolters Kluwer Medknow Publications, 2018. |
| سنة النشر: | 2018 |
| المجموعة: | LCC:Dentistry |
| مصطلحات موضوعية: | Calcium chloride, calcium silicate, periapical, root-end filling materials, root-end filling, solubility, Dentistry, RK1-715 |
| الوصف: | Aims: Evaluation and comparison of solubility, pH, and calcium ion release of calcium-silicate based root-end filling materials mineral trioxide aggregate (MTA) and biodentine. Methodology: The total sample size for the study was 120. Sixty samples were for solubility of MTA and biodentine and sixty for pH and calcium ion release of MTA and biodentine. MTA and biodentine were added to sixty stainless steel ring molds. The mass of 60 dried glass bottles was measured. Shifting of samples to bottles containing 5 mL of distilled water was done and was stored for 24 h. The bottles were dried at 105°C and weighed. This procedure was repeated for 3, 10, 30, and 60 days. Data obtained for solubility were analyzed with independent t-test. Sixty polyethylene tubes 1 mm long were filled with MTA and biodentine and placed in lidded flasks containing 10 mL distilled water and were preserved in an oven at 37°C. After 2 h, the flasks were removed from hot air oven, and the water was assessed for pH and calcium ion release. pH readings were performed with an pH Meter. Atomic absorption spectrophotometer was used for the detection of calcium ion release. Preservation of the tubes containing the cements was done in new flasks containing 10 mL of distilled water for further detection of pH and calcium ion release in the different time periods of 6, 24 h and 7, 28 days, respectively. Data were analyzed with independent t-test. Results: Significantly higher solubility was exhibited for biodentine for 30 and 60 days than MTA. Statistical difference was observed between the solubility, pH, and calcium ion release values of MTA and biodentine. Conclusions: Biodentine exhibited higher solubility, pH, and calcium ion release in comparison with MTA. |
| نوع الوثيقة: | article |
| وصف الملف: | electronic resource |
| اللغة: | English |
| تدمد: | 0976-4003 2231-2293 |
| Relation: | http://www.ijds.in/article.asp?issn=0976-4003;year=2018;volume=10;issue=4;spage=197;epage=202;aulast=Kumari; https://doaj.org/toc/0976-4003; https://doaj.org/toc/2231-2293 |
| DOI: | 10.4103/IJDS.IJDS_42_18 |
| URL الوصول: | https://doaj.org/article/5e904e11d442452192eff8c725167ff4 |
| رقم الأكسشن: | edsdoj.5e904e11d442452192eff8c725167ff4 |
| قاعدة البيانات: | Directory of Open Access Journals |
Full Text Finder | تدمد: | 09764003 22312293 |
|---|---|
| DOI: | 10.4103/IJDS.IJDS_42_18 |