Hydrogen Embrittlement of 27Cr−4Mo−2Ni Super Ferritic Stainless Steel
العنوان: | Hydrogen Embrittlement of 27Cr−4Mo−2Ni Super Ferritic Stainless Steel |
---|---|
المؤلفون: | Fei Yang, Yujin Nie, Huiyun Zhang, Weiqiang Niu, Quanxin Shi, Jinyao Ma, Liuwei Zheng, Wei Liang |
المصدر: | Materials, Vol 17, Iss 7, p 1546 (2024) |
بيانات النشر: | MDPI AG, 2024. |
سنة النشر: | 2024 |
المجموعة: | LCC:Technology LCC:Electrical engineering. Electronics. Nuclear engineering LCC:Engineering (General). Civil engineering (General) LCC:Microscopy LCC:Descriptive and experimental mechanics |
مصطلحات موضوعية: | super ferritic stainless steel, hydrogen embrittlement, mechanical properties, yield strength, fracture behavior, Technology, Electrical engineering. Electronics. Nuclear engineering, TK1-9971, Engineering (General). Civil engineering (General), TA1-2040, Microscopy, QH201-278.5, Descriptive and experimental mechanics, QC120-168.85 |
الوصف: | The effect of hydrogen content on the deformation and fracture behavior of 27Cr−4Mo−2Ni super ferritic stainless steel (SFSS) was investigated in this study. It was shown that the plasticity and yield strength of SFSS were very susceptible to hydrogen content. The introduction of hydrogen led to a significant decrease in elongation and a concurrent increase in yield strength. Nevertheless, a critical threshold was identified in the elongation reduction, after which the elongation remained approximately constant even with more hydrogen introduced, while the yield strength exhibited a monotonic increase with increasing hydrogen content within the experimental range, attributed to the pinning effect of the hydrogen Cottrell atmosphere on dislocations. Furthermore, the hydrogen-charged SFSS shows an apparent drop in flow stress after upper yielding and a reduced work hardening rate during the subsequent plastic deformation. The more hydrogen is charged, the more the flow stress drops, and the lower the work hardening rate becomes. |
نوع الوثيقة: | article |
وصف الملف: | electronic resource |
اللغة: | English |
تدمد: | 1996-1944 |
Relation: | https://www.mdpi.com/1996-1944/17/7/1546; https://doaj.org/toc/1996-1944 |
DOI: | 10.3390/ma17071546 |
URL الوصول: | https://doaj.org/article/609d859cc26e4a14984c16d1b46d62a6 |
رقم الأكسشن: | edsdoj.609d859cc26e4a14984c16d1b46d62a6 |
قاعدة البيانات: | Directory of Open Access Journals |
تدمد: | 19961944 |
---|---|
DOI: | 10.3390/ma17071546 |