Effect of Additives on the Dispersion Properties of Aqueous Based C/LiFePO4 paste and its Impact on Lithium Ion Battery High Power Properties
العنوان: | Effect of Additives on the Dispersion Properties of Aqueous Based C/LiFePO4 paste and its Impact on Lithium Ion Battery High Power Properties |
---|---|
المؤلفون: | Jin-Hyon Lee, Hyun-Ho Kim, Sung-Bok Wee, Ungyu Paik |
المصدر: | KONA Powder and Particle Journal, Vol 27, Iss 0, Pp 239-245 (2014) |
بيانات النشر: | Hosokawa Powder Technology Foundation, 2014. |
سنة النشر: | 2014 |
المجموعة: | LCC:Technology (General) LCC:Nuclear and particle physics. Atomic energy. Radioactivity |
مصطلحات موضوعية: | lithium ion battery, olivine, poly (acrylic acid), dispersion, electrochemical properties, Technology (General), T1-995, Nuclear and particle physics. Atomic energy. Radioactivity, QC770-798 |
الوصف: | Aqueous-based C/LiFePO4 positive electrodes with high-rate capabilities are described with an intended application in lithium ion batteries. Pastes consisting of C/LiFePO4 particles, sodium carboxymethyl cellulose (CMC), water-soluble elastomeric binder (WSB) and poly (acrylic acid) (PAA) were prepared in an aqueous medium and tape-cast onto an aluminum foil. It was found that the incorporation of PAA significantly decreased the apparent viscosity of the C/LiFePO4 paste as well as shifted particle size distribution to lower value, which resulted in an improvement of the C/LiFePO4 dispersion properties. A correlation was made between the dispersion properties and the electrochemical properties. The electrochemical properties indicated that the electrode with PAA exhibited a discharge specific capacity above 70 mAhg−1 at 20C, which was about seven times higher than the discharge specific capacity without PAA at 20C which showed a discharge specific capacity of only 10 mAhg−1. This was attributed to the formation of a resistance-imparting agglomeration, which is consistent with the dispersion properties of C/LiFePO4 particles. |
نوع الوثيقة: | article |
وصف الملف: | electronic resource |
اللغة: | English |
تدمد: | 0288-4534 2187-5537 |
Relation: | https://www.jstage.jst.go.jp/article/kona/27/0/27_2009022/_pdf/-char/en; https://doaj.org/toc/0288-4534; https://doaj.org/toc/2187-5537 |
DOI: | 10.14356/kona.2009022 |
URL الوصول: | https://doaj.org/article/c6b5d752c9f945418ccf9bf9c023bfce |
رقم الأكسشن: | edsdoj.6b5d752c9f945418ccf9bf9c023bfce |
قاعدة البيانات: | Directory of Open Access Journals |
تدمد: | 02884534 21875537 |
---|---|
DOI: | 10.14356/kona.2009022 |