Weldability of ductile cast iron using AISI-316L stainless steel ER rod
العنوان: | Weldability of ductile cast iron using AISI-316L stainless steel ER rod |
---|---|
المؤلفون: | Javier Cárcel Carrasco, Fidel Salas Vicente, Aurora Martínez Corral, Manuel Pascual Guillamón |
المصدر: | Revista de Metalurgia, Vol 58, Iss 3 (2022) |
بيانات النشر: | Consejo Superior de Investigaciones Científicas, 2022. |
سنة النشر: | 2022 |
المجموعة: | LCC:Mining engineering. Metallurgy |
مصطلحات موضوعية: | AISI-316L, Annealing, Cast iron, Corrosion, Preheat, Weldability, Mining engineering. Metallurgy, TN1-997 |
الوصف: | This paper analyzes the corrosion resistance and the mechanical and microstructural properties of a welded joint of ductile cast iron using AISI316L stainless steel as filler material and three different heat treatments: preheating at 250 and 450 ºC and a post-weld annealing treatment. The results show the presence of ledeburite at the interface between the weld bead and the heat affected zone and at the root pass, along with a loss of strength and ductility when the welding coupons are preheated. An annealing does not eliminate the presence of ledeburite and leads to a massive precipitation of chromium carbides at the areas of the weld bead where dilution is higher. Corrosion rate was lower for the annealed coupon, but in that case, the corrosion of the weld bead increases due to the precipitation of chromium carbides. |
نوع الوثيقة: | article |
وصف الملف: | electronic resource |
اللغة: | English Spanish; Castilian |
تدمد: | 0034-8570 1988-4222 |
Relation: | https://revistademetalurgia.revistas.csic.es/index.php/revistademetalurgia/article/view/1543; https://doaj.org/toc/0034-8570; https://doaj.org/toc/1988-4222 |
DOI: | 10.3989/revmetalm.224 |
URL الوصول: | https://doaj.org/article/71c889b7607a4c859568e497cebb3658 |
رقم الأكسشن: | edsdoj.71c889b7607a4c859568e497cebb3658 |
قاعدة البيانات: | Directory of Open Access Journals |
تدمد: | 00348570 19884222 |
---|---|
DOI: | 10.3989/revmetalm.224 |