Step solution treatment of a wire-arc directed energy deposited Al-Zn-Mg-Cu alloy: defects suppression and mechanical property improvement
العنوان: | Step solution treatment of a wire-arc directed energy deposited Al-Zn-Mg-Cu alloy: defects suppression and mechanical property improvement |
---|---|
المؤلفون: | Bolun Dong, Xiaoyu Cai, Yunhao Xia, Fukang Chen, Sanbao Lin, Debin Shan, Yingying Zong |
المصدر: | Virtual and Physical Prototyping, Vol 19, Iss 1 (2024) |
بيانات النشر: | Taylor & Francis Group, 2024. |
سنة النشر: | 2024 |
المجموعة: | LCC:Science LCC:Manufactures |
مصطلحات موضوعية: | Wire-arc directed energy deposition, heat treatment, step solution, defect, Science, Manufactures, TS1-2301 |
الوصف: | Wire-arc directed energy deposition is promising for manufacturing ultra-high-strength Al-Zn-Mg-Cu alloy components. However, the undesired microstructure and performance of as-deposited alloys make the heat treatment a mandatory post-process, which still lacks systematic investigation. This work aims to establish a comprehensive understanding of it. An interplay between second-phase dissolution and defect formation in the single-stage solution of as-deposited Al-Zn-Mg-Cu alloy was found: as solution temperatures increase, the equilibrium proportion of residual phases decreases, but the proportion of pore defects increases significantly. Based on a systematic full-factor solution test, a 430°C/4 h + 450°C/4 h step solution process was proposed, which suppressed the pore defects by about 54.8% while keeping the effect of the residual phase dissolution unchanged. After the step solution and artificial aging, the average yield strength of the alloy reached 475 MPa, and the elongation reached 6.5%, showing 201.6% and 85.7% improvement compared with the as-deposited state, respectively. |
نوع الوثيقة: | article |
وصف الملف: | electronic resource |
اللغة: | English |
تدمد: | 17452759 1745-2767 1745-2759 |
Relation: | https://doaj.org/toc/1745-2759; https://doaj.org/toc/1745-2767 |
DOI: | 10.1080/17452759.2024.2382170 |
URL الوصول: | https://doaj.org/article/7900302989794b6f8611cd54ccdd82c0 |
رقم الأكسشن: | edsdoj.7900302989794b6f8611cd54ccdd82c0 |
قاعدة البيانات: | Directory of Open Access Journals |
تدمد: | 17452759 17452767 |
---|---|
DOI: | 10.1080/17452759.2024.2382170 |