Effect of sintering temperature on microstructures and mechanical properties of ZK60 magnesium alloys
العنوان: | Effect of sintering temperature on microstructures and mechanical properties of ZK60 magnesium alloys |
---|---|
المؤلفون: | Luosheng Ma, Lili Ma, Peipeng Jin, Xinya Feng, Lei Jia |
المصدر: | Materials Research Express, Vol 9, Iss 1, p 016514 (2022) |
بيانات النشر: | IOP Publishing, 2022. |
سنة النشر: | 2022 |
المجموعة: | LCC:Materials of engineering and construction. Mechanics of materials LCC:Chemical technology |
مصطلحات موضوعية: | magnesium alloy, hot-press sintering, microstructure, mechanical property, chemical composition, Materials of engineering and construction. Mechanics of materials, TA401-492, Chemical technology, TP1-1185 |
الوصف: | In this study, ZK60 Mg alloys were prepared via hot-press sintering under a constant pressure of 30 MPa as well as Ar atmosphere. The sintering temperature was determined to be in the range of 450 °C–600 °C with an interval of 50 °C. The effect of sintering temperature on the microstructures and mechanical properties of the alloys was investigated. All the four sintered alloys mainly exhibited an α -Mg-phase structure and equiaxed grain microstructure. However, a specific amount of melt, enriched in Zn element, formed when the sintering temperature reached 500 °C. Thus, only the alloy sintered at 450 °C maintained the nominal composition of the alloy powder, and exhibited the favorable yield strength and hardness, which was 135.1 MPa and 57 HV, respectively. The alloys sintered at 550 °C and 600 °C exhibited a reduced yield strength and hardness due to the loss of Zn element. |
نوع الوثيقة: | article |
وصف الملف: | electronic resource |
اللغة: | English |
تدمد: | 2053-1591 |
Relation: | https://doaj.org/toc/2053-1591 |
DOI: | 10.1088/2053-1591/ac47c7 |
URL الوصول: | https://doaj.org/article/8fea9e1cd27b48b3afe8a632f5e0b063 |
رقم الأكسشن: | edsdoj.8fea9e1cd27b48b3afe8a632f5e0b063 |
قاعدة البيانات: | Directory of Open Access Journals |
تدمد: | 20531591 |
---|---|
DOI: | 10.1088/2053-1591/ac47c7 |