Objectives: This study aimed to evaluate the effects of hydrofluoric acid (HF) concentration and etching time on the surface roughness (SR) and three-point flexural strength of Suprinity and to analyze the surface elements before and after etching. Materials and Methods: To measure the SR, 70 specimens of Suprinity (2×4×5mm3) were assigned to seven groups (n=10). Six groups were etched for 20, 60, and 120 seconds with 5% and 10% HF and 7th group was the control group. Specimens were evaluated using atomic force microscopy (AFM). One specimen from each group was used to analyze the surface elements using scanning electron microscopy (SEM). For measuring the three-point flexural strength, 60 specimens were divided into six groups (n=10) and etched as previously described. The flexural strength was measured using a universal testing machine. T-test, one-way analysis of variance (ANOVA), and two-way ANOVA were used for statistical analyses (P