دورية أكاديمية
Diamond-Like-Carbon Coated Dies for Electromagnetic Embossing
العنوان: | Diamond-Like-Carbon Coated Dies for Electromagnetic Embossing |
---|---|
المؤلفون: | Marius Herrmann, Björn Beckschwarte, Henning Hasselbruch, Julian Heidhoff, Christian Schenck, Oltmann Riemer, Andreas Mehner, Bernd Kuhfuss |
المصدر: | Materials, Vol 13, Iss 21, p 4939 (2020) |
بيانات النشر: | MDPI AG, 2020. |
سنة النشر: | 2020 |
المجموعة: | LCC:Technology LCC:Electrical engineering. Electronics. Nuclear engineering LCC:Engineering (General). Civil engineering (General) LCC:Microscopy LCC:Descriptive and experimental mechanics |
مصطلحات موضوعية: | impulse forming, adhesion, micro hard milling, hardened tool steel, a-C:H coating, Technology, Electrical engineering. Electronics. Nuclear engineering, TK1-9971, Engineering (General). Civil engineering (General), TA1-2040, Microscopy, QH201-278.5, Descriptive and experimental mechanics, QC120-168.85 |
الوصف: | Electromagnetic forming is a high-speed process, which features contactless force transmission. Hence, punching operations can be realized with a one-sided die and without a mechanical punch. As the forces act as body forces in the part near the surface, the process is especially convenient for embossing microstructures on thin sheet metals. Nevertheless, the die design is critical concerning wear like adhesion. Several die materials were tested, like aluminum, copper as well as different steel types. For all die materials adhesion phenomena were observed. To prevent such adhesion an a-C:H-PVD (Physical Vapor Deposition)-coating was applied to steel dies (X153CrMoV12) and tested by embossing aluminum sheets (Al99.5). By this enhancement of the die adhesion was prevented. Furthermore, the die surface was structured with tribology-effective patterns that were generated by micro hard milling. The embossing quality was topographically analyzed with respect to different initial surface states of the sheets. It was identified that thicker sheets facilitate better embossing results. Moreover, the initial sheet surface has a decisive influence on the embossing quality, whereby the characteristic of the topography showed different susceptibility on the initial sheet surface state. |
نوع الوثيقة: | article |
وصف الملف: | electronic resource |
اللغة: | English |
تدمد: | 1996-1944 |
Relation: | https://www.mdpi.com/1996-1944/13/21/4939; https://doaj.org/toc/1996-1944 |
DOI: | 10.3390/ma13214939 |
URL الوصول: | https://doaj.org/article/93959d5df6804e288f3712c7595f4219 |
رقم الأكسشن: | edsdoj.93959d5df6804e288f3712c7595f4219 |
قاعدة البيانات: | Directory of Open Access Journals |
تدمد: | 19961944 |
---|---|
DOI: | 10.3390/ma13214939 |