Effect of Two Different Ultrafast Curing Exposure Durations on the Surface Hardness of Bulk Fill Composite - An In-Vitro Study
العنوان: | Effect of Two Different Ultrafast Curing Exposure Durations on the Surface Hardness of Bulk Fill Composite - An In-Vitro Study |
---|---|
المؤلفون: | Shekar Shobana, Anandavelu Sujareetha, Sundaresan Balagopal, Sarath Kumar, Sriganesh Angusamy, Sebatni Anisha |
المصدر: | Indian Journal of Dental Research, Vol 34, Iss 4, Pp 438-442 (2024) |
بيانات النشر: | Wolters Kluwer Medknow Publications, 2024. |
سنة النشر: | 2024 |
المجموعة: | LCC:Dentistry |
مصطلحات موضوعية: | high-intensity curing, surface hardness, ultrafast curing, vicker’s microhardness, Dentistry, RK1-715 |
الوصف: | Aim: The aim of the present study is to assess the microhardness of resin-based composites (RBCs) cured with ultrafast curing mode at two different exposure durations. Study Design: This is an experimental in-vitro study. Forty-five cylindrical composite specimens were prepared to a dimension of 5 mm height and 4 mm diameter. Curing was done using three different exposure modes and duration with dual mode LED curing light as follows: Group I: Ultrafast curing mode for 1 second at 2300 mW/cm2 (n = 15); Group II: Ultrafast curing mode for 3 second at 2300 mW/cm2 (n = 15) and Group III: Standard exposure mode for 20 second at 1000 mW/cm2 (n = 15). Vicker’s microhardness measurement was done on both the curing and non-curing sides of the specimen using a motorised diamond-faced micro-indenter (Wilson Wolpwert, Germany) using a load of 50 gram and a dwell time of 30 second. Statistical Analysis: Kruskal Wallis ANOVA was used to test for difference between the three groups followed by Mann–Whitney U test for post-hoc analysis. Results: The microhardness values of the composite cured with a conventional curing unit were significantly higher than the ultrafast cured specimens. Conclusion: Low-intensity conventional curing lights were found to perform better than the high-intensity ultrafast curing units. |
نوع الوثيقة: | article |
وصف الملف: | electronic resource |
اللغة: | English |
تدمد: | 0970-9290 1998-3603 |
Relation: | https://journals.lww.com/10.4103/ijdr.ijdr_5_23; https://doaj.org/toc/0970-9290; https://doaj.org/toc/1998-3603 |
DOI: | 10.4103/ijdr.ijdr_5_23 |
URL الوصول: | https://doaj.org/article/96468668074f4f90b62aab6db104e77f |
رقم الأكسشن: | edsdoj.96468668074f4f90b62aab6db104e77f |
قاعدة البيانات: | Directory of Open Access Journals |
تدمد: | 09709290 19983603 |
---|---|
DOI: | 10.4103/ijdr.ijdr_5_23 |