Effect of Current Density on the Microstructure and Mechanical Properties of 3YSZ/Al2O3 Composites by Flash Sintering
العنوان: | Effect of Current Density on the Microstructure and Mechanical Properties of 3YSZ/Al2O3 Composites by Flash Sintering |
---|---|
المؤلفون: | Yujie Bai, Ying Zhang, Zhifeng Tian, Junzhan Zhang, Zongmo Shi |
المصدر: | Materials, Vol 15, Iss 9, p 3110 (2022) |
بيانات النشر: | MDPI AG, 2022. |
سنة النشر: | 2022 |
المجموعة: | LCC:Technology LCC:Electrical engineering. Electronics. Nuclear engineering LCC:Engineering (General). Civil engineering (General) LCC:Microscopy LCC:Descriptive and experimental mechanics |
مصطلحات موضوعية: | flash sintering, eutectic structure, grain size, 3YSZ/Al2O3, Technology, Electrical engineering. Electronics. Nuclear engineering, TK1-9971, Engineering (General). Civil engineering (General), TA1-2040, Microscopy, QH201-278.5, Descriptive and experimental mechanics, QC120-168.85 |
الوصف: | The 3YSZ/40 wt% Al2O3 composites were prepared by flash sintering at a low furnace temperature (700 °C). The effects of the current density on the relative density and Vickers hardness of the composites were systematically investigated. The results showed that the relative densities and Vickers hardness of the samples increased gradually with the increasing of the current densities, and the relative density was as high as 94.2%. The Vickers hardness of 11.3 GPa was obtained under a current density of 102 mA/mm2. Joule heating and defects generation are suggested to be the main causes of rapid densification in flash sintering. The microstructure of the molten zone showed the formation of eutectic structures in the composite, suggesting that grain boundary overheating may have contributed to the formation of the molten zone. |
نوع الوثيقة: | article |
وصف الملف: | electronic resource |
اللغة: | English |
تدمد: | 1996-1944 |
Relation: | https://www.mdpi.com/1996-1944/15/9/3110; https://doaj.org/toc/1996-1944 |
DOI: | 10.3390/ma15093110 |
URL الوصول: | https://doaj.org/article/e9f7ff1df86e428d9f71df72dad608a9 |
رقم الأكسشن: | edsdoj.9f7ff1df86e428d9f71df72dad608a9 |
قاعدة البيانات: | Directory of Open Access Journals |
تدمد: | 19961944 |
---|---|
DOI: | 10.3390/ma15093110 |