Effect of Blending Method on the Mechanical Properties of Wood-Plastic Composites
العنوان: | Effect of Blending Method on the Mechanical Properties of Wood-Plastic Composites |
---|---|
المؤلفون: | M. Chaharmahali, S. Kazemi Najafi, M. Tajvidi |
المصدر: | علوم و تکنولوژی پلیمر, Vol 20, Iss 4, Pp 361-367 (2007) |
بيانات النشر: | Iran Polymer and Petrochemical Institute, 2007. |
سنة النشر: | 2007 |
مصطلحات موضوعية: | wood-plastic composite, mdf, mechanical properties, melt blend, dry blend, Polymers and polymer manufacture, TP1080-1185 |
الوصف: | In this study, the possibility of producing wood-plastic panels was studied using two different blending methods including melt blend and dry blend. Wood-plastic panels were made from recycled high density polyethylene (as resin) and MDF waste (as natural fiber) at 60, 70 and 80% by weight filler loading. Nominal density and dimensions of the panels were 1g/cm3 and 35×35×1 cm, respectively. The mechanical properties of the panels including flexural elastic modulus, flexural strength, screw and nail withdrawal resistance, and impact strength were studied. Maximum values of flexural modulus of wood-plastic panels were found at 70% fiber content in both methods. Flexural strength, screw and nail withdrawal resistance and impact strength of wood-plastic composites reduced with the increase in fiber content from 60% to 80%. Mechanical properties of samples made with dry blend method were generally higher than those of samples made with melt blend method for all corresponding formulations. |
نوع الوثيقة: | article |
وصف الملف: | electronic resource |
اللغة: | Persian |
تدمد: | 1016-3255 2008-0883 |
Relation: | http://jips.ippi.ac.ir/article_785_028193c26985321f3791d48b59a5c932.pdf; https://doaj.org/toc/1016-3255; https://doaj.org/toc/2008-0883 |
DOI: | 10.22063/jipst.2007.785 |
URL الوصول: | https://doaj.org/article/ef65a6dd399f422595bf7e9817ca654d |
رقم الأكسشن: | edsdoj.f65a6dd399f422595bf7e9817ca654d |
قاعدة البيانات: | Directory of Open Access Journals |
تدمد: | 10163255 20080883 |
---|---|
DOI: | 10.22063/jipst.2007.785 |