This work concerns the verification of the self-healing ability of PP-co-HUPy copolymers dispersed in epoxy systems. PP is the acronym for the Poly-PEGMA polymer, and HUPy refers to the HEMA-UPy copolymers based on ureidopyrimidinone (UPy) moieties. In particular, this work aims to verify whether this elastomer characterized by an intrinsic self-healing ability can activate supramolecular interactions among polymer chains of an epoxy resin, as in the elastomer alone. The elastomer includes a class of polyethylene glycol monomethyl ether methacrylate-based copolymers, with different percentages of urea-N-2-amino-4-hydroxy-6-methyl pyrimidine-N’-(hexamethylene-n-carboxyethyl methacrylate) (HEMA-UPy) co-monomers. The self-healing capability of these copolymers based on possible quadruple hydrogen bond interactions between polymer chains has been verified. The formulated epoxy samples did not show self-healing efficiency. This can be attributed to the formation of phase segregation that originates during the curing process of the samples, although the PP-co-HUPy copolymers are completely soluble in the liquid epoxy matrix EP. The morphological investigation highlighted the presence of crystals of PP-co-HUPy copolymers, which are in greater quantity in the sample containing the highest weight percentage (7.8 wt%) of HUPy units. Furthermore, the crystals act as promotors for increasing the curing degree (DC) of the epoxy systems containing HUPy units. DC goes from 91.6% for EP to 96.1% and 95.4% for the samples containing weight percentages of 2.5 and 7.8 wt% of HUPy units, respectively. Dynamic mechanical analysis (DMA) shows storage modulus values for epoxy systems containing PP-co-HUPy units lower than that of the unfilled resin EP. The values of maximum in Tan δ (Tg), representing the temperature at which the glass transition occurs, are 220 for the unfilled resin EP, 228 for the sample containing 2.5 wt% of HEMA-UPy units, and 211 for the sample containing 7.8 wt% of HEMA-UPy units.
Full Text Finder