Investigation of Multi-Cold Rolling Passes on Mechanical Characteristics and Surface Quality of AlCuV Alloy
العنوان: | Investigation of Multi-Cold Rolling Passes on Mechanical Characteristics and Surface Quality of AlCuV Alloy |
---|---|
المؤلفون: | Nabeel Abu Shaban, Safwan M Al-Qawabah, Hashem S. Alkhaldi |
المصدر: | Advances in Sciences and Technology, Vol 17, Iss 5, Pp 68-76 (2023) |
بيانات النشر: | Lublin University of Technology, 2023. |
سنة النشر: | 2023 |
المجموعة: | LCC:Engineering (General). Civil engineering (General) |
مصطلحات موضوعية: | copper, vanadium, surface roughness, materials processing, rolling passes, angle orientation, Engineering (General). Civil engineering (General), TA1-2040 |
الوصف: | In this study, the effect of rolling angle orientation namely; 0, 45, and 90 degrees, and three rolling passes on the mechanical behavior of Al-Cu after vanadium addition were investigated. Al-4%Cu and Al-4%Cu-0.1%V sheets were produced and rolled from 4 mm to 3 mm followed by 3 to 2 mm, and finally from 2 mm to 1.3 mm. After each pass, the tensile test was performed in three directions from which the maximum tensile force, deformation energy, microhardness, and average surface roughness (Ra) were determined. A pronounce finding is that the addition of both additions of 0.1% vanadium to Al-4%Cu alloy and multi-rolling passes resulted in reducing the deformation energy by 85.4, and the maximum tensile forces reduced by 56.6%, this resulted in reduction of production cost of AlCuV alloys, furthermore, it resulted in reducing the anisotropy of AlCuV alloy. Additionally, the average microhardness was enhanced for Al-Cu and AlCuV alloy, whereas the Ra was in maximum enhanced for AlCuV alloy of about 64.9%. |
نوع الوثيقة: | article |
وصف الملف: | electronic resource |
اللغة: | English |
تدمد: | 2080-4075 2299-8624 22998624 |
Relation: | http://www.astrj.com/Investigation-of-Multi-Cold-Rolling-Passes-on-Mechanical-Characteristics-and-Surface,171265,0,2.html; https://doaj.org/toc/2080-4075; https://doaj.org/toc/2299-8624 |
DOI: | 10.12913/22998624/171265 |
URL الوصول: | https://doaj.org/article/fd6d952bfbdc4986896d5a5ff2d1a42e |
رقم الأكسشن: | edsdoj.fd6d952bfbdc4986896d5a5ff2d1a42e |
قاعدة البيانات: | Directory of Open Access Journals |
تدمد: | 20804075 22998624 |
---|---|
DOI: | 10.12913/22998624/171265 |