EFFECTS OF AGGREGATE CONTENT ON THE INTERCONNECTED PORE FORMATION AND PROPERTIES OF POROUS PURGING PLUG MATERIALS
العنوان: | EFFECTS OF AGGREGATE CONTENT ON THE INTERCONNECTED PORE FORMATION AND PROPERTIES OF POROUS PURGING PLUG MATERIALS |
---|---|
المؤلفون: | Qingheng Wang, Anping Dong, Qiu Wendong, Li Yuanbing, Ruan Guozhi, Zhang Lanqin |
المصدر: | Ceramics-Silikáty, Vol 63, Iss 4, Pp 374-379 (2019) |
بيانات النشر: | University of Chemistry and Technology, Prague, 2019. |
سنة النشر: | 2019 |
المجموعة: | LCC:Clay industries. Ceramics. Glass |
مصطلحات موضوعية: | firing temperature, aluminum hydroxide, microstructure, Clay industries. Ceramics. Glass, TP785-869 |
الوصف: | The physical properties and microstructure of porous purging plug materials with different aggregate contents and prepared at different firing temperatures were investigated by means of X-ray diffraction, scanning electron microscopy, air permeability, pore size distribution, apparent porosity, bulk density, cold modulus of rupture (CMOR), cold elastic modulus (E) and cold crushing strength (CCS) tests. The results show that the aggregate content had a great effect on the interconnected pore formation and properties of porous purging plug materials. With decreasing aggregate content, the apparent porosity and air permeability increased due to the distance between aggregates increasing and Al(OH)₃ formation, and the pore size distributions changed from a monomodal distribution to a bimodal distribution. The higher temperature facilitated the formation of a denser structure and interconnected pores. In addition, the CCS and porosity were found to follow a simple exponential relationship. When the apparent porosity increased, the CCS decreased, and vice versa |
نوع الوثيقة: | article |
وصف الملف: | electronic resource |
اللغة: | English |
تدمد: | 0862-5468 1804-5847 |
Relation: | http://www.ceramics-silikaty.cz/index.php?page=cs_detail_doi&id=1284; https://doaj.org/toc/0862-5468; https://doaj.org/toc/1804-5847 |
DOI: | 10.13168/cs.2019.0033 |
URL الوصول: | https://doaj.org/article/fe11ab79474a4ffe909e4963b5839305 |
رقم الأكسشن: | edsdoj.fe11ab79474a4ffe909e4963b5839305 |
قاعدة البيانات: | Directory of Open Access Journals |
تدمد: | 08625468 18045847 |
---|---|
DOI: | 10.13168/cs.2019.0033 |