Ferrium M54 Steel
| العنوان: | Ferrium M54 Steel |
|---|---|
| المصدر: | DTIC |
| بيانات النشر: | 2015-03-18 |
| تفاصيل مُضافة: | NAVAL AIR WARFARE CENTER AIRCRAFT DIV PATUXENT RIVER MD Lee, E U Stanley, M Pregger, B Lei, C Lipnickas, E |
| نوع الوثيقة: | Electronic Resource |
| مستخلص: | Bare and Zn-14% Ni alloy coated Ferrium M54 steels were studied to clarify their mechanical, fatigue, and stress corrosion cracking (SCC) properties. Compared to the currently available high strength and high toughness steel, AerMet 100, this steel has much greater SCC resistance, but similar mechanical properties and susceptibility to corrosion fatigue. The Zn-14% Ni alloy coating appears to provide the steel some protection against hydrogen embrittlement/SCC and corrosion fatigue in aqueous 3.5% NaCl solution of pH 7.3. The fatigue crack growth mechanisms of the bare and coated steels are striation formation in air, and a combination of striation formation and intergranular cracking in aqueous 3.5% NaCl solution. The original document contains color images. |
| مصطلحات الفهرس: | Properties of Metals and Alloys, Mechanics, MECHANICAL PROPERTIES, STEEL, COATINGS, COMPARISON, CORROSION, CRACKING(FRACTURING), FATIGUE(MECHANICS), FRACTOGRAPHY, HYDROGEN EMBRITTLEMENT, NICKEL ALLOYS, STRESSES, ZINC ALLOYS, FERRIUM M54, SCC(STRESS CORROSION CRACKING), ZINC1 4 PERCENT NICKEL ALLOY COATINGS, AERMET 100 STEEL, FATIGUE CRACK GROWTH, BARE STEELS, COATED STEELS, BARE M54, COATED M54, Text |
| URL: | |
| الإتاحة: | Open access content. Open access content Approved for public release; distribution is unlimited. |
| ملاحظة: | text/html English |
| أرقام أخرى: | DTICE ADA614146 913596647 |
| المصدر المساهم: | From OAIster®, provided by the OCLC Cooperative. |
| رقم الأكسشن: | edsoai.ocn913596647 |
| قاعدة البيانات: | OAIster |
| الوصف غير متاح. |