Efficient and novel Sb2S3 based solar cells with chitosan/poly(ethylene glycol)/electrolyte blend
العنوان: | Efficient and novel Sb2S3 based solar cells with chitosan/poly(ethylene glycol)/electrolyte blend |
---|---|
المصدر: | International Journal of Energy Research |
بيانات النشر: | 2018 |
تفاصيل مُضافة: | Lojpur, Vesna Krstić, Jelena Kačarević-Popović, Zorica M. Mitrić, Miodrag Rakočević, Zlatko Lj. Validžić, Ivana Lj. |
نوع الوثيقة: | Electronic Resource |
مستخلص: | We present here a novel solar cell made of ITO/composite p-doped Sb2S3 + P3HT + PANI + TiO2/amorphous Sb2S3+P3HT+PANI+TiO2/n-doped Sb2S3 + P3HT + PANI + TiO2/solid carrier/aluminum as counter electrode. With spraying technique, the layers were deposited and the thickness of films was 1m. A new solid carrier of electrolyte was a blend consisted of chitosan (low MW), polyethylene glycol and electrolyte. X-ray diffraction was recorded to confirm the amorphous nature of the blend. Information about the surface appearance and roughness of a solid carrier dry and soaked in the electrolyte was given by atomic force microscopy. The solar cell was examined at very low and low light intensity (5% and 35% of sun, respectively), and at standard test conditions (100% of sun) using different light sources. The whole cell surface was 7.5cm(2) while the illuminated part was 3cm(2). Obtained results expressed for the illuminated surface showed the highest efficiency of 23.1% at 5% of sun while the efficiency of the cell was 2.9% at 35% of sun and only 0.75% at intensity of 100% of sun. |
مصطلحات الفهرس: | CS/PEG/electrolyte blend, low light intensity, Sb2S3, solar cell, article |
URL: | info:eu-repo/grantAgreement/MESTD/Integrated and Interdisciplinary Research (IIR or III)/45005/RS |
الإتاحة: | Open access content. Open access content ARR restrictedAccess |
ملاحظة: | International Journal of Energy Research |
أرقام أخرى: | RSPST oai:vinar.vin.bg.ac.rs:123456789/1915 0363-907X 1099-114X https://vinar.vin.bg.ac.rs/handle/123456789/1915 000422754000038 10.1002/er.3899 2-s2.0-85030104934 1363253997 |
المصدر المساهم: | UIVERSITY OF BELGRADE From OAIster®, provided by the OCLC Cooperative. |
رقم الأكسشن: | edsoai.on1363253997 |
قاعدة البيانات: | OAIster |
الوصف غير متاح. |